Product

Mix viscosity
(mPa·s,25℃)

Heat release peak time
(min)

TG(℃)

Characteristic

SWANCOR

RB208-A/BS

600～1300

≥115

SWANCOR EzCicloRB208-A/BS is a two-component epoxy resin system. It has the characteristics of slower medium temperature viscosity increase rate and faster high-temperature reactivity, making it more suitable for winding extruded profiles and large components.

EzCicloRB208-A/BS is a recyclable resin, and the cured product can be treated to separate the resin and fibers. The separated fibers and resin can be reused in composite materials.

SWANCOR

RB208-A/BV

400～1000

-

≥110

SWANCOR EzCicloRB208-A/BV is a two-component epoxy resin system. It has the advantages of low viscosity, long operation time, good operability, and good curing transparency. Moreover, it can cure quickly under appropriate temperature settings and has excellent mechanical properties. Excellent adhesion between carbon fiber and glass fiber makes it suitable for the extrusion and winding of transparent composite components such as insulation core rods, glass plates, and carbon plates.

EzCicloRB208-A/BV is a recyclable resin, and the cured product can be treated to separate the resin and fibers. The separated fibers and resin can be reused in composite materials.

SWANCOR

RB508-A/B

600～1300

-

≥110

SWANCOR EzCicloRB508-A/B is a two-component epoxy resin system. It has the advantages of low viscosity, long operation time, and good operability. It can cure quickly at the appropriate temperature setting and has excellent mechanical properties. For carbon fiber and glass fiber, they have excellent adhesion, making them particularly suitable for composite material components in extrusion molding processes, such as insulation core rods, glass plates, and carbon plates.

RB508-A/B is a recyclable resin, and the cured board can be treated to separate the resin and fibers. The separated fibers and resin can be reused in composite materials.

SWANCOR

RB511-A/BS

200～300

330～480

≥75

The EzCiclo RB511 series is a recyclable room temperature curing vacuum infusion (SCRMIP and RTM) resin system composed of a special epoxy resin main agent and curing agent, which is particularly suitable for processing applications of wind turbine blades, yachts, and large structural products. Its main characteristics and advantages are low viscosity, moderate gelation time, excellent mechanical properties, high HDT, and good fiber (glass fiber/carbon fiber) wettability.

SWANCOR

RB513-1A/BF

700～950

(LVT#3-60rpm

35～60

> 70

SWANCOR EzCiclo RB513-1A/BF is a recyclable room temperature curing hand paste special resin composed of a special epoxy resin main agent and curing agent, which is particularly suitable for the processing and application of wind turbine blades, yachts, and large structural products. Its main characteristics and advantages are suitable operating viscosity and operating time, as well as good wettability to glass fiber and carbon fiber.

SWANCOR

RB513-A/BS

800～1200

20～60

≥75

The SWANCOR EzCiclo RB513 series is a recyclable room temperature curing hand paste special resin composed of a special epoxy resin main agent and a curing agent. It is particularly suitable for the processing and application of fan blades, yachts, and large structural products. Its main characteristics and advantages are suitable operating viscosity, adjustable gelation time, and good wettability to glass fiber and carbon fiber.

The SWANCOR EzCiclo RB513 series is equipped with curing agents with different curing speeds to meet the requirements for different operating times; And the mixing ratio of different curing agents is the same, so different curing agents can be mixed according to special needs to achieve customized operation time and facilitate use.

Product

Mix viscosity
(mPa·s,70℃)

Heat release peak time
(min)

TG(℃)

Characteristic

SWANCOR

RH512

80 to 200*1

50 to 80*2

54～58

SWANCOR RH512 is a tough, low viscosity, and recyclable high-performance free radical cured resin. Designed for closed mold application processes, such as vacuum infusion with suitable reinforcement materials and core materials. Composite components formed using SWANCOR RH512 can achieve good degradation efficiency by using the recommended biodegradable treatment.

SWANCOR

RH513

400 to 800*3

30 to 40*4

53～57

SWANCOR RH513 is a tough, thixotropic, and recyclable high-performance free radical cured resin. Designed for open mold application processes, such as hand lay up layers with suitable reinforcement materials and core materials. Composite components formed using SWANCOR RH513 can achieve good degradation efficiency by using the recommended biodegradable treatment.

SWANCOR

RB553

15000～25000

150℃ : 3 to 8

120℃ : 13-18

120～130

SWANCOR EzCiclo RB553 is a recyclable hot-melt epoxy resin for pre impregnated materials. The formula does not contain Diuron or volatile components, making it safer and healthier to use. Resin has good compatibility with various reinforcing fiber materials, good impregnation, and can achieve better mechanical strength. The carbon fiber and glass fiber pre impregnated materials made of it are suitable for various sports equipment, such as bicycles, rackets, fishing rods, and baseball bats; Wait. In addition, it can also be applied in other fields such as industrial use, automobile and locomotive industry, aerospace, medical, shipbuilding, as well as 3C products, building reinforcement, and so on.

SWANCOR

RB556

40000～50000

150℃ : 3 to 8

120℃ : 13-18

"120

SWANCOR EzCiclo RB556 is a hot melt epoxy resin used for recyclable prepreg. The formula does not contain Diuron or volatile components, making it safer and healthier to use. Resin has good compatibility with various reinforcing fiber materials, good impregnation, and can achieve better mechanical strength. The carbon fiber and glass fiber pre impregnated materials made from it are suitable for various sports equipment, such as bicycles, rackets, fishing rods, baseball bats, etc. In addition, it can also be applied in other fields such as industrial use, automobile and locomotive industry, aerospace, medical, shipbuilding, as well as 3C products, building reinforcement, and so on.

SWANCOR

RB564

28000～38000

150℃ : 3 to 8

120℃ : 13-18

"120

SWANCOR EzCiclo RB564 is a hot melt epoxy resin used for recyclable prepreg. The formula does not contain Diuron or volatile components, making it safer and healthier to use. Resin has good compatibility with various reinforcing fiber materials, good impregnation, and can achieve better mechanical strength. The carbon fiber and glass fiber pre impregnated materials made from it are suitable for various sports equipment, such as bicycles, rackets, fishing rods, baseball bats, etc. In addition, it can also be applied in other fields such as industrial use, automobile and locomotive industry, aerospace, medical, shipbuilding, as well as 3C products, building reinforcement, and so on.

SWANCOR

RB730-A/B

400～550

(LVT#2-30 RPM

120 to 160*1

≥70

SWANCOR EzCiclo RB730 is an epoxy resin adhesive developed specifically for curing processes at room temperature. It is composed of a special epoxy resin main agent and a curing agent, and is particularly suitable for bonding applications between epoxy resin composite materials and metal materials that require room temperature curing processes. Its main characteristics and advantages are: long operation applicability, fast curing speed, and the ability to achieve curing at room temperature or under heating conditions; Good adhesion between epoxy composite materials, between metals, and between metals and epoxy composite materials; Good liquidity, excellent operability, and outstanding mechanical properties.